Jiangsu Huayang Nylon Co., Ltd. is an innovative enterprise focusing on the production, sales and service of new polymer materials, engineering plastics, nylon plastic parts and polyester yarn. Huayang nylon has many large-scale production bases in the local area.
Key words: nylon 66 slice | engineering modified plastics | nylon cable ties
Detailed parameters
劲旅环境
PA66B30
Characteristics
·Natural color, 30% fiberglass reinforced
·Excellent comprehensive mechanical performance
Application
·Aviation and metallurgical fields
·The automotive industry
·Engineering/Industrial Accessories
Typical properties
| Properties | Test method | Test conditio | S.I Units |
Typical Values |
| Physical property | ||||
| Filler content | ISO3451 | % | 30 | |
| Specific gravity | ISO1183 | 23℃ | g/cm³ | 1.36 |
| Mold shrinkage | ISO294 | 23℃ | % | 0.3-0.6 |
| Water absorption | ISO62 | 23℃,24h 2mm |
% | 0.7 |
| Mechanical property | ||||
| Tensile strength | ISO527 | 5mm/min | MPa | 185 |
| Flexural strengt | ISO178 | 2mm/min | MPa | 273 |
| Flexural modulus | ISO178 | 2mm/min | MPa | 8450 |
| Impact strength,notched | ISO179 | 23℃ | kJ/m² | 12 |
| Impact strength,unnotched | ISO179 | 23℃ | kJ/m² | 80 |
| Thermal property | ||||
| Heat Distortion Temp | ISO75 | 1.80MPa | ℃ | 249 |
| Flammability | ||||
| Flammability | UL94 | CLASS | HB | |
| Electrical | ||||
| Surface resistivity | IEC60093 | Ω.cm | 1015 | |
Note：The above data are typical, as reference only
Processing Conditions
| Barrel Zone Temr | Rear | 270℃ | 260-280℃ |
| Center | 280℃ | 270-290℃ | |
| Front | 290℃ | 280-310℃ | |
| Mold Temp | 60℃ | 65-90℃ | |
| Processing Temp.Limit | 315℃ | ||
| Injection Speed | Medium to high speed | ||
| Injection Pressure | 50-100MPa | ||
| Packing pressure | 30-50MPa | ||
| Packing time | 1-5S | ||
| Pre-Dry Requirements | 90-120℃,4-6h | ||
The above data is for reference only for injection molding machines. The above process can be adjusted appropriately according to different models, molds, and product requirements.
HK8G30E
Characteristics
·Natural color, 30% fiberglass reinforced
·Excellent comprehensive mechanical performance
Application
·Aviation and metallurgical fields
·The automotive industry
·Engineering/Industrial Accessories
Typical properties
| Properties | Test method | Test conditio | S.I Units |
Typical Values |
| Physical property | ||||
| Filler content | ISO3451 | % | 30 | |
| Specific gravity | ISO1183 | 23℃ | g/cm³ | 1.341 |
| Mold shrinkage | ISO294 | 23℃ | % | 0.3-0.8 |
| Water absorption | ISO62 | 23℃,24h 2mm |
% | 0.7 |
| Mechanical property | ||||
| Tensile strength | ISO527 | 5mm/min | MPa | 158 |
| Flexural strengt | ISO178 | 2mm/min | MPa | 237 |
| Flexural modulus | ISO178 | 2mm/min | MPa | 7780 |
| Impact strength,notched | ISO179 | 23℃ | kJ/m² | 17.8 |
| Impact strength,unnotched | ISO179 | 23℃ | kJ/m² | 80 |
| Thermal property | ||||
| Heat Distortion Temp | ISO75 | 1.80MPa | ℃ | 75 |
| Flammability | ||||
| Flammability | UL94 | CLASS | HB | |
| Electrical | ||||
| Surface resistivity | IEC60093 | Ω.cm | 1015 | |
Note：The above data are typical, as reference only
Processing Conditions
| Barrel Zone Temr | Rear | 27 5℃ | 270-285℃ |
| Center | 285℃ | 280-290℃ | |
| Front | 295℃ | 290-300℃ | |
| Mold Temp | 70℃ | 65-100℃ | |
| Processing Temp.Limit | 315℃ | ||
| Injection Speed | Medium to high speed | ||
| Injection Pressure | 50-100MPa | ||
| Packing pressure | 30-50MPa | ||
| Packing time | 1-5S | ||
| Pre-Dry Requirements | 100-13 0℃,4-6h | ||
The above data is for reference only for injection molding machines. The above process can be adjusted appropriately according to different models, molds, and product requirements.
Product Consulting
Mobile website QR code
Huayang Nylon
Jiangsu Huayang Nylon Co., Ltd.
Fax: +86-513-88461688
E-mail:
Address: Group 8, Maozhuang Village, Duntou Town, Hai 'an City, Nantong City, Jiangsu Province