Product Description
HYPA6-108
①Raw material description
| Specification level | Injection grade | Exterior color | Porcelain white granules |
| Purpose Overview | Special material for cable clamp | ||
| Instruction manual | New material, V0 flame retardant, high toughness, halogen-containing, dyeable | ||
②Technical data of raw materials
| Performance item | Test Methods | Test Data | Data unit |
| Tensile Strength |
ISO527 |
40 |
MPa |
| Elongation at break |
ISO527 |
12 |
% |
| Bending strength |
ISO178 |
66 |
MPa |
| Izod notched impact strength |
ISO180 |
8 |
KJ/m2 |
| Density |
ISO1183 |
1.18 |
g/cm3 |
| Rockwell hardness |
ISO2093/2 |
110 |
- |
| Melting point |
ISO3416 |
215 |
℃ |
| Heat distortion temperature/0.45mpa |
ISO75 |
170 |
℃ |
| Flame retardancy |
UL-94 |
V0 |
- |
| Surface resistivity |
ISO167 |
1013 |
Ω |
| Filling amount | Burning method |
5 |
% |
HYPA6-109
①Raw material description
| Specification level | Injection grade | Exterior color | Porcelain white granules |
| Purpose Overview | Electronic and electrical connectors, housings, etc. | ||
| Instruction manual | New material, halogen-free flame retardant, V0 grade, Can be dyed | ||
②Technical data of raw materials
| Performance item | Test Methods | Test Data | Data unit |
| Tensile Strength |
ISO527 |
70 |
MPa |
| Elongation at break |
ISO527 |
12 |
% |
| Bending strength |
ISO178 |
90 |
MPa |
| Izod notched impact strength |
ISO180 |
5 |
KJ/m2 |
| Density |
ISO1183 |
1.15 |
g/cm3 |
| Rockwell hardness |
ISO2093/2 |
115 |
- |
| Melting point |
ISO3416 |
220 |
℃ |
| Heat distortion temperature/0.45mpa |
ISO75 |
140 |
℃ |
| Flame retardancy |
UL-94 |
V0 |
- |
| Surface resistivity |
ISO167 |
1013 |
Ω |
| Filling amount | Burning method |
0 |
% |
HYPA6-110
①Raw material description
| Specification level | Injection grade | Exterior color | Black or brown particles |
| Purpose Overview | Electronic and electrical connectors, switch boxes, etc. | ||
| Instruction manual | New material, halogen-free flame retardant, V0 grade | ||
②Technical data of raw materials
| Performance item | Test Methods | Test Data | Data unit |
| Tensile Strength |
ISO527 |
58 |
MPa |
| Elongation at break |
ISO527 |
7 |
% |
| Bending strength |
ISO178 |
75 |
MPa |
| Izod notched impact strength |
ISO180 |
5 |
KJ/m2 |
| Density |
ISO1183 |
1.2 |
g/cm3 |
| Rockwell hardness |
ISO2093/2 |
115 |
- |
| Melting point |
ISO3416 |
225 |
℃ |
| Heat distortion temperature/0.45mpa |
ISO75 |
170 |
℃ |
| Flame retardancy |
UL-94 |
V0 |
- |
| Surface resistivity |
ISO167 |
1013 |
Ω |
| Filling amount | Burning method |
3 |
% |
PA6MCA
Characteristics
·Natural color, flame retardant
·Excellent comprehensive mechanical performance
Application
·Aviation and metallurgical fields
·The automotive industry
·Engineering/Industrial Accessories
Typical properties
| Properties | Test method | Test condition | S.I.Units | Typical Values |
| Physical property | ||||
| Filler content | ISO3451 | % | 0 | |
| Specific gravity | ISO1183 | 23℃ | g/cm³ | 1.177 |
| Mold shrinkage | ISO294 | 23℃ | % | 0.3-0.6 |
| Water absorption | ISO62 | 23℃,24h 2mm |
% | 0.7 |
| Mechanical property | ||||
| Tensile strength | ISO527 | 5mm/min | MPa | 72 |
| Flexural strength | ISO178 | 2mm/min | MPa | 90 |
| Flexural modulus | ISO178 | 2mm/min | MPa | 2200 |
| Impact strength,notched | ISO179 | 23℃ | kJ/m2 | 4.8 |
| Impact strength,unnotched | ISO179 | 23℃ | kJ/m² | 105 |
| Thermal property | ||||
| Heat Distortion Temp | ISO75 | 1.80MPa | ℃ | 75 |
| Flammability | ||||
| Flammability | UL94 | CLASS | V1 | |
| Electrical | ||||
| Surface resistivity | IEC60093 | Ω.cm | 1015 | |
Note：The above data are typical, as reference only
Processing Conditions
| Barrel Zone Temp | Rea | 230℃ | 220-235℃ |
| Center | 240℃ | 230-245℃ | |
| Front | 245℃ | 240-255℃ | |
| Mold Temp | 70℃ | 65-90℃ | |
| Processing Temp.Limit | 275℃ | ||
| Injection Speed | Medium to high speed | ||
| Injection Pressure | 50-100MPa | ||
| Packing pressure | 30-50MPa | ||
| Packing time | 1-5S | ||
| Pre-Dry Requirements | 90-120℃,4-6h | ||
The above data is for reference only for injection molding machines. The above process can be adjusted appropriately according to different models, molds, and product requirements.
Huayang Nylon uses its own unique production process and technology to develop and produce five series of independent intellectual property products such as nylon 66 slices, nylon reinforced and toughened slices, nylon ties, polyester sewing threads, and polyester sewing threads., High-speed rail, clothing, industrial packaging and other industries.
Since its establishment, Huayang Nylon has always paid attention to technological development and independent innovation. At present, it has a research and development team led by a young team; at the same time, it has jointly established an industry-university-research practice base with many famous colleges and universities, and established a long-term relationship with famous enterprises at home and abroad. Technical cooperation relationship.
Mobile website QR code
Huayang Nylon
Jiangsu Huayang Nylon Co., Ltd.
Fax: +86-513-88461688
E-mail:
Address: Group 8, Maozhuang Village, Duntou Town, Hai 'an City, Nantong City, Jiangsu Province