Flame retardant nylon PA66
Classification:
Jiangsu Huayang Nylon Co., Ltd. is an innovative enterprise focusing on the production, sales and service of new polymer materials, engineering plastics, nylon plastic parts and polyester yarn. Huayang nylon has many large-scale production bases in the local area.
Key words: nylon 66 slice | engineering modified plastics | nylon cable ties
Detailed parameters
劲旅环境
HYPA66-107
①Raw material description
| Specification level | Injection grade | Exterior color | Porcelain white granules |
| Purpose Overview | Safe box, auto parts, etc. | ||
| Instruction manual | New material, halogen-free flame retardant, dyeable | ||
②Technical data of raw materials
| Performance item | Test Methods | Test Data | Data unit |
| Tensile Strength |
ISO527 |
75 |
MPa |
| Elongation at break |
ISO527 |
4.5 |
% |
| Bending strength |
ISO178 |
100 |
MPa |
| Izod notched impact strength |
ISO180 |
6 |
KJ/m2 |
| Density |
ISO1183 |
1.14 |
g/cm3 |
| Rockwell hardness |
ISO2093/2 |
118 |
- |
| Melting point |
ISO3416 |
258 |
℃ |
| Heat distortion temperature/0.45mpa |
ISO75 |
200 |
℃ |
| Flame retardancy |
UL-94 |
V0 |
- |
| Surface resistivity |
ISO167 |
1013 |
Ω |
| Filling amount | Burning method |
0 |
% |
HYPA66-108
①Raw material description
| Specification level | Injection grade | Exterior color | Black particles |
| Purpose Overview | Electronic connectors, cable clamps, etc. | ||
| Instruction manual | New material, halogen flame retardant, toughened, dyeable | ||
②Technical data of raw materials
| Performance item | Test Methods | Test Data | Data unit |
| Tensile Strength |
ISO527 |
55 |
MPa |
| Elongation at break |
ISO527 |
8 |
% |
| Bending strength |
ISO178 |
80 |
MPa |
| Izod notched impact strength |
ISO180 |
10 |
KJ/m2 |
| Density |
ISO1183 |
1.2 |
g/cm3 |
| Rockwell hardness |
ISO2093/2 |
110 |
- |
| Melting point |
ISO3416 |
255 |
℃ |
| Heat distortion temperature/0.45mpa |
ISO75 |
210 |
℃ |
| Flame retardancy |
UL-94 |
V0 |
- |
| Surface resistivity |
ISO167 |
- |
Ω |
| Filling amount | Burning method |
0 |
% |
HYPA66-109
①Raw material description
| Specification level | Injection grade | Exterior color | Black particles |
| Purpose Overview | Electronic and electrical connectors, fuse boxes, etc. | ||
| Instruction manual | New material, halogen-free flame retardant | ||
②Technical data of raw materials
| Performance item | Test Methods | Test Data | Data unit |
| Tensile Strength |
ISO527 |
75 |
MPa |
| Elongation at break |
ISO527 |
4 |
% |
| Bending strength |
ISO178 |
100 |
MPa |
| Izod notched impact strength |
ISO180 |
8 |
KJ/m2 |
| Density |
ISO1183 |
1.18 |
g/cm3 |
| Rockwell hardness |
ISO2093/2 |
118 |
- |
| Melting point |
ISO3416 |
255 |
℃ |
| Heat distortion temperature/0.45mpa |
ISO75 |
215 |
℃ |
| Flame retardancy |
UL-94 |
V0 |
- |
| Surface resistivity |
ISO167 |
1013 |
Ω |
| Filling amount | Burning method |
0 |
% |
PA66MCA
Characteristics
·Natural color, flame retardant
·Excellent comprehensive mechanical performance
Application
·Aviation and metallurgical fields
·The automotive industry
·Engineering/Industrial Accessories
Typical properties
| Properties | Test method | Test condition | S.I.Units | Typical Values |
| Physical property | ||||
| Filler content | ISO3451 | % | 0 | |
| Specific gravity | ISO1183 | 23℃ | g/cm³ | 1.179 |
| Mold shrinkage | ISO294 | 23℃ | % | 0.3-0.6 |
| Water absorption | ISO62 | 23℃,24h 2mm |
% | 0.7 |
| Mechanical property | ||||
| Tensile strength | ISO527 | 5mm/min | MPa | 75 |
| Flexural strength | ISO178 | 2mm/min | MPa | 92 |
| Flexural modulus | ISO178 | 2mm/min | MPa | 2280 |
| Impact strength,notched | ISO179 | 23℃ | kJ/m2 | 5 |
| Impact strength,unnotched | ISO179 | 23℃ | kJ/m² | 103 |
| Thermal property | ||||
| Heat Distortion Temp | ISO75 | 1.80MPa | ℃ | 249 |
| Flammability | ||||
| Flammability | UL94 | CLASS | V1 | |
| Electrical | ||||
| Surface resistivity | IEC60093 | Ω.cm | 1015 | |
Note：The above data are typical, as reference only
Processing Conditions
| Barrel Zone Temp | Rea | 270℃ | 260-280℃ |
| Center | 280℃ | 270-290℃ | |
| Front | 290℃ | 280-310℃ | |
| Mold Temp | 60℃ | 65-90℃ | |
| Processing Temp.Limit | 315℃ | ||
| Injection Speed | Medium to high speed | ||
| Injection Pressure | 50-100MPa | ||
| Packing pressure | 30-50MPa | ||
| Packing time | 1-5S | ||
| Pre-Dry Requirements | 90-120℃,4-6h | ||
The above data is for reference only for injection molding machines. The above process can be adjusted appropriately according to different models, molds, and product requirements.
Product Consulting
Mobile website QR code
Huayang Nylon
Jiangsu Huayang Nylon Co., Ltd.
Fax: +86-513-88461688
E-mail:
Address: Group 8, Maozhuang Village, Duntou Town, Hai 'an City, Nantong City, Jiangsu Province